Fatigue crack growth in the vicinity of a grain boundary modelled using a discrete dislocation technique
It is well known that the behaviour of short cracks differs from that of long cracks due to the relatively large plastic zone and strong influence from the surrounding microstructure, and for very low growth rates, it is important to account for discrete dislocations within the material. In this study, a discrete dislocation model is presented for the study of the growth behaviour of a short edge